SPECIFICATION                   (Reference sheet)

· Supplier   : Samsung electro-mechanics

· Samsung P/N :

CL31A226KAHNNWE

· Product   : Multi-layer Ceramic Capacitor

· Description   :

CAP, 22㎌, 25V, ±10%, X5R, 1206


A. Samsung Part Number

                                                           CL      31       A      226      K        A       H       N        N       W           E







① ② ③ ④ ⑤ ⑥ ⑦ ⑧ ⑨ ⑩ ⑪


① Series

Samsung Multi-layer Ceramic Capacitor




② Size

1206       (inch code)               L   :   3.20±0.20㎜


W :

1.60±0.20㎜

③   Dielectric

④   Capacitance

⑤   Capacitance tolerance

⑥   Rated Voltage

⑦   Thickness

X5R

22㎌

±10% 25V

1.60±0.20㎜

⑧     Inner electrode

Termination   Plating

⑨     Product

⑩     Special

⑪    Packaging



Ni

Cu

Ni/Sn 100%            (Pb Free)

Normal

Industrial   (Network,Power,etc)

Embossed Type, 7" Reel / Quantity : 2K








B. Structure & Dimension



Samsung P/N



Dimension(㎜)


L

W

T

BW

CL31A226KAHNNWE

3.20±0.20

1.60±0.20

1.60±0.20

0.50±0.30



Judgement

Test condition

Capacitance

 Within specified tolerance

120㎐±20% / 0.5±0.1Vrms

*A   capacitor prior to measuring the capacitance is heat treated at 150℃+0/-10℃ for 1hour and   maintained in ambient air for 24±2 hours.

Tan δ (DF)

0.1 max.

Insulation

Resistance

10,000㏁ or 100㏁·㎌  Whichever is smaller

Rated Voltage   60~120 sec


Appearance

 No abnormal exterior appearance

Microscope   (×10)


Withstanding

Voltage

 No dielectric breakdown or  mechanical breakdown

250% of the   rated voltage


Temperature

Characteristics

X5R

(From -55℃ to 85℃, Capacitance   change should be within ±15%)


Adhesive Strength of   Termination

 No peeling shall be occur on the  terminal electrode

500g·f, for   10±1 sec.


Bending Strength

Capacitance   change : within ±10%

Bending to the limit (1mm)

with 1.0mm/sec.   (2mm bending outgoing test)


Solderability

More   than 95% of terminal surface  is to be   soldered newly

SnAg3.0Cu0.5 solder 245±5℃, 3±0.3sec.

(preheating :   80~120℃ for 10~30sec.)



Resistance   to

Soldering Heat

Capacitance   change : within ±7.5%  Tan δ, IR :   initial spec.

Solder pot :   270±5℃, 10±1sec.



Vibration Test

Capacitance   change : within ±5%  Tan δ, IR :   initial spec.

Amplitude : 1.5mm

From 10㎐ to 55㎐ (return :   1min.)

2hours × 3   direction (x, y, z)



Moisture

Resistance

Capacitance change : within   ±12.5% Tan δ : 0.125 max.

IR : 500㏁ or 12.5㏁·㎌

         Whichever is smaller

With rated voltage

65±2℃,90±5%RH,   500hrs+12/-0hrs



High   Temperature

Resistance

Capacitance change : within   ±12.5% Tan δ : 0.125 max.

IR : 1,000㏁ or 25㏁·㎌

         Whichever is smaller

With 150% of the rated   voltage

Max. operating temperature

1,000+48/-0hrs



Temperature

Cycling

Capacitance   change : within ±7.5%  Tan δ, IR :   initial spec.

1 cycle condition

Min. operating   temperature  

→ Max. operating   temperature

5 cycle test

→

→

25℃

25℃